Davenport, Washington | I am sorry, if you welded that up for me I would be yelling at you until you were crying. But then I am a pretty good welder and picky. But then again I always say if you can work for me then you can work for anybody. And I started out making welds just like yours 40 years ago. My opinion is that if that machine will be subjected to the same stress as before it will break your welds again faster. You also didn't listen or didn't understand others on the first post as to v shaped patch iron. Also I would try to use 7018 AC on your buzz box which I see in the back ground. The beatiful thing is that on iron you can grind it all off and try again over and over if you let it cool slowly each time. | |
|